回火温度对SA533B钢组织和力学性能的影响 |
| |
引用本文: | 周光杰,赵爱民,武会宾,蔡阿云. 回火温度对SA533B钢组织和力学性能的影响[J]. 中国材料科技与设备, 2011, 0(6): 80-82 |
| |
作者姓名: | 周光杰 赵爱民 武会宾 蔡阿云 |
| |
作者单位: | [1]北京科技大学高效轧制国家工程研究中心,北京100083 [2]北京首钢冷轧薄板有限公司,北京101304 |
| |
摘 要: | 通过光学显微镜和透射电镜,研究了不同回火温度对SA533B钢力学性能、组织及析出行为的影响。结果表明,SA533B钢经880~C淬火和680~C回火后综合力学性能最佳,屈服强度、抗拉强度和延伸率分别为635MPa、750MPa和21%,冲击功120J。
|
关 键 词: | SA533B 回火 性能 组织 |
Effect of Tempering Temperature on Microstructure and Mechanical Properties of SA533B Steel |
| |
Affiliation: | ZHOU Guang--jie , ZHAO Ai--min, WU Hui--bin, CAI A--yun(1. National Engineering Research Center of Advanced Rolling, University of Science and Technology Beijing, Beijing, 100083, China; 2. Beijing shuogang cold rolling CO LTD, Beijing, 101304, China) |
| |
Abstract: | The effects of tempering temperature on the mechanical properties, microstructure and precipitation behavior of SA533B steel were investigated by utilizing optical microscopy and transmission electron microscopy. The results show that the optimized comprehensive mechanical properties were obtained after quenched at 880℃ and tempered at 680℃, and yield strength, ultimate tensile strength, total elongation and impact energy can reach 635MPa, 750MPa, 21% and 120J. |
| |
Keywords: | SA533B Tempering Property Microstructure |