Synthesis of nanosized tungsten carbide from phenol formaldehyde resin coated precursors |
| |
Authors: | LUO Ji GUO Zhimeng GAO Yuxi LIN Tao |
| |
Affiliation: | School of Materials Science and Engineering,University of Science and Technology Beijing,Beijing 100083,China |
| |
Abstract: | Nanosized tungsten carbide was synthesized from phenol formaldehyde resin (PF) coated tungsten precursors.The process has three steps in which nanosized tungsten particles were first coated with PF,then the precursors were carburized at 950℃,and finally the carburized powders were treated in flowing wet hydrogen atmosphere at 940℃ to remove the uncombined carbon.The obtained powders were characterizedusing X-ray diffraction analysis (XRD),field-emission scanning electron microscopy (FESEM),small angle X-ray scattering (SAXS),andcombustion-gas-volume method.The results indicated that single-phase WC could be synthesized using excessive PF as carburizer at a muchlower temperature compared with using mixed carbon black.After wet hydrogen treating,the mean size of the obtained WC particles was 94.5nm and the total carbon content was 6.18 wt.%. |
| |
Keywords: | cemented carbide nanosized tungsten carbide carburization phenol formaldehyde resin |
本文献已被 维普 万方数据 ScienceDirect 等数据库收录! |
|