Application of Rietveld Refinement to Investigate the High Chromium White Cast Iron Austempered at Different Temperatures |
|
| Authors: | HOU Qing-yu HUANG Zhen-yi WANG Jing-tao |
| Affiliation: | 1. School of Materials Scienee and Engineering, Nanjing University of Science and Technology, Nanjing 210094,Jiangsu, China;School of Materials Science and Engineering, Anhui University of Technology,Ma'anshan 243002, Anhui, China 2. School of Materials Science and Engineering, Anhui University of Technology,Ma'anshan 243002, Anhui, China 3. School of Materials Scienee and Engineering, Nanjing University of Science and Technology, Nanjing 210094,Jiangsu, China |
| Abstract: | The effect of austempering temperature on the microstructure and properties of a high chromium white cast iron was investigated with the Rietveld refinement method. The result shows that the upper bainite exists in the sample austempered at 623 K and the martensite, lower bainite, M7C3, and retained austenite exist in the samples austempered at 563 K and 593 K. The relative content of the retained austenite increases with increasing the austempering temperature from 563 K to 623 K. The higher hardness, impact toughness and impact abrasive wear resistance can be obtained for the specimen austempered at 593 K. |
| Keywords: | high chromium white cast iron austempering retained austenite Rietveld refinement microstructure properties |
| 本文献已被 维普 万方数据 ScienceDirect 等数据库收录！ | |
| 点击此处可从《钢铁研究学报(英文版)》浏览原始摘要信息 | |
| 点击此处可从《钢铁研究学报(英文版)》下载全文 | |