Ni0.5Zn0.5Fe2O4 nanoparticles and their magnetic properties and adsorption of bovine serum albumin

Ni_0.5Zn_0.5Fe₂O₄ nanoparticles were synthesized by the facile citrate-gel process and the preliminary measurement for adsorption of bovine serum albumin (BSA) protein on these nanoparticles was carried out. The gel precursor and resultant nanoparticles were characterized by TG-DSC, FTIR, XRD, TEM and VSM techniques and the BSA adsorption on the nanoparticles was analyzed by UV spectrophotometer at room temperature. The results show that the single phase of spinel Ni_0.5Zn_0.5Fe₂O₄ is formed at 400 °C. With increasing calcination temperature from 400 to 700 °C, the average grain size increases from about 14 to 45 nm and consequently, the specific saturation magnetization of Ni_0.5Zn_0.5Fe₂O₄ nanoparticles increases from about 46 to 68 Am²/kg. The coercivity initially increases and then decreases with increasing calcination temperature, with a maximum value 9.2 kA/m at 500 °C. The as-prepared Ni_0.5Zn_0.5Fe₂O₄ nanoparticles exhibit a good adsorbing ability for BSA and the optimized adsorption is achieved for the Ni_0.5Zn_0.5Fe₂O₄ nanoparticles calcined at 500 °C with grain size about 24 nm.