Crystal Growth and Dielectric Properties of New Ferroelectric Barium Titanate: BaTi2O5

Single crystals of the ferroelectric BaTi₂O₅ and BaTiO₃ were prepared from a solution of 33-mol% BaO and 67-mol% TiO₂ by a rapid cooling method. The dielectric constant () and dielectric loss tangent (tan) were measured in a wide temperature range of 10–860 K and in a frequency range of 0.1–3,000 kHz. The along the b-axis of the BaTi₂O₅ crystal, prepared in air, shows a sharp dielectric anomaly reaching 30,000 at the ferroelectric Curie temperature of T_C = 752 K. By contrast, the crystal prepared in a reducing atmosphere shows a diffuse phase transition near T_C = 703 K. The values of and tan are compared between these three crystals consisting of two kinds of BaTi₂O₅ and one BaTiO₃.