| 气压机管线应力腐蚀检测及机理分析 |
| |
| 引用本文： | 郝相敏.气压机管线应力腐蚀检测及机理分析[J].石油化工设备技术,2001,22(3):29-31,55. |
| |
| 作者姓名： | 郝相敏 |
| |
| 作者单位： | 大连西太平洋石油化工有限公司, |
| |
| 摘 要： | 对重油加氢脱硫装置的3-CP-01酸性气压缩机不锈钢管线发生应力腐蚀开裂进行了分析，结果表明是由于H
|
| 关 键 词： | 不锈钢 酸性气 应力腐蚀开裂 |
| 文章编号： | 1006-8805(2001)03-0029-03 |
| 修稿时间： | 2000年10月23 |
STRESS CORROSION DETECTION
AND MECHANISM ANALYSIS ON AIR COMPERSSOR PIPING |
| |
| Hao Xiangmin.STRESS CORROSION DETECTION
AND MECHANISM ANALYSIS ON AIR COMPERSSOR PIPING[J].Petro-Chemical Equipment Technology,2001,22(3):29-31,55. |
| |
| Authors: | Hao Xiangmin |
| |
| Affiliation: | Hao Xiangmin.Dalian west pacific petrochemical Co Ltd.,P.C 116600 |
| |
| Abstract: | The stress corrosion crack occured on stainless steel piping of 3 cp 01 sour gas compressor for heavy oil hydrodesulphated unit was analized.The result shows that the sulfur stress corrosion crack was caused by H 2 and H 2S.In accordance with that specific condition,the effective prevention was given. |
| |
| Keywords: | Stainless steel Sour gas Stress corrosion crack |