Ni–SiO2 and Ni–Fe–SiO2 catalysts for methane decomposition to prepare hydrogen and carbon filaments

Active and stable Ni–Fe–SiO₂ catalysts prepared by sol–gel method were employed for direct decomposition of undiluted methane to produce hydrogen and carbon filaments at 823 K and 923 K. The results indicated that the lifetime of Ni–Fe–SiO₂ catalysts was much longer than Ni–SiO₂ catalyst at a higher reaction temperature such as 923 K, however, a reverse trend was shown when methane decomposition took place at a lower reaction temperature such as 823 K. XRD studies suggested that iron atoms had entered into the Ni lattice and Ni–Fe alloy was formed in Ni–Fe–SiO₂ catalysts. The structure of the carbon filaments generated over Ni–SiO₂ and Ni–Fe–SiO₂ was quite different. TEM studies showed that “multi-walled” carbon filaments were formed over 75%Ni–25%SiO₂ catalyst, while “bamboo-shaped” carbon filaments generated over 35%Ni–40%Fe–25%SiO₂ catalysts at 923 K. Raman spectra of the generated carbons demonstrated that the graphitic order of the “multi-walled” carbon filaments was lower than that of the “bamboo-shaped” carbon filaments.