| Abstract: | Two component interpenetrating polymer networks (IPN) of the SIN type (simultaneous interpenetrating networks), composed of a polystyrene network (crosslinked with divinyl benzene) and a polyester-polyurethane network (crosslinked with trimethylolpropane), were made. Electron microscopy and glass-transition measurements showed that phase separation had resulted with some interpenetration, presumably occurring at the boundaries. At a composition of about 75 percent polyurethane, a phase inversion occurred, the continuous phase being polystyrene at polyurethane compositions of less than 75 percent. The stress-strain properties and hardness measurements agreed with these results. Enhanced tensile strength was observed in the IPN's in a concentration range where modulus reinforcement was not evident. A small enhancement in tear strength and thermal stability was also noted. |