Influence of Hydrogen on the Formation of Fatigue Thresholds in Structural Steels

We analyze certain phenomena related to the influence of gaseous hydrogen and hydrogen dissolved in a metal on the near-threshold growth of fatigue cracks. The significant decrease in crack growth resistance due to the action of hydrogen as compared with that in vacuum is caused mainly by the adsorption decrease in strength due to adsorption. We established three factors of the ambiguous influence of hydrogen on the effective fatigue threshold K _theff, for which a positive influence is replaced by a negative one, namely: the strength level, temperature of testing, and high-temperature degradation of the metal. The following fractographic peculiarities of the near-threshold growth of cracks in a degraded metal are revealed: the local tunneling along the front of a crack and the presence of fatigue grooves. We propose a mechanism of crack closure due to both roughness and the component of longitudinal shear at the tip of the crack. We analyze the scale effect of fatigue thresholds, determine the conditions for invariance of the parameter K _theff under conditions of plane deformation, and established the dependence of K _theff on the thickness of specimens in the case of tests of a hydrogenated degraded metal.