Synthesis and Characterization of Aurivillius Phases in the Bi–Ag–Ti–O System

New Aurivillius phases in the Bi–Ag–Ti–O system were investigated by means of a solid-state reaction and X-ray diffraction. We found that the oxygen partial pressure has a significant influence on the synthesis of the Aurivillius phases. The mixed-layer Aurivillius phase Ag_0.5Bi_8.5Ti₇O₂₇ was observed after firing in an O₂ flow, but a single-phase material is difficult to obtain. A single-phase compound of the four-layer Aurivillius phase Ag_0.5Bi_4.5Ti₄O₁₅ was obtained on firing in an oxygen partial pressure of 10 bar (1 × 10⁶ Pa). The dielectric properties (at 1 MHz) of the Ag_0.5Bi_4.5Ti₄O₁₅ compound were as follows: T _max=687°C, ? _r =166 (～20°C), and tan δ=0.004 (～20°C).