Structure and multiferroic properties of ternary (1?x)(0.8BiFeO3-0.2BaTiO3)-xK0.5Na0.5NbO3 (0?≤?x?≤?0.5) solid solutions

The ternary (1?x)(0.8BiFeO_3-0.2BaTiO₃)-xK_0.5Na_0.5NbO₃ (0?≤?x?≤?0.5) solid solutions have been successfully synthesized by a solid-state reaction route. X-ray diffraction and Rietveld refinement studies reveal the phase transition from the rhombohedral and tetragonal phases to the single tetragonal phase with x increasing. The average grain size decreases initially and then increases as x increases, whereas the remnant magnetization shows an opposite trend and reaches the maximum value of ~2.09?emu/g at x?=?0.3. An enhanced remnant polarization of ~8.6?μC/cm² appears at x?=?0.3 due to the structure distortion and the decrement of defects. Moreover, the remanent polarization and the relative permittivity reach the maximum value of ~20.14 μC/cm² (10?Hz) and ~644 (1?kHz) at x?=?0.5, respectively, and the corresponding dielectric loss decreases to the lowest value of ~0.022 (1?kHz). These results indicate that the properties of ternary BFO-BTO-KNN solid solutions can be modulated by adjusting the K_0.5Na_0.5NbO₃ content to adapt to different application needs.