Upconversion and infrared luminescences in Er/Yb codoped Y2O3 and (Y0.9La0.1)2O3 transparent ceramics

Er³⁺ and Yb³⁺ codoped Y₂O₃ and (Y_0.9La_0.1)₂O₃ transparent ceramics were fabricated by the conventional ceramics processing with nanopowders. Compared to Er/Yb:Y₂O₃, Er/Yb:(Y_0.9La_0.1)₂O₃ ceramics had higher transmittance. Intense upconversion (UC) and infrared emission (1543 nm) were observed under excitation of 980 nm. According to three intensity parameters Ω₂, Ω₄, and Ω₆ fitted by the Judd-Ofelt theory, the spectroscopic quality parameters (X), radiative lifetimes (τ_rad), and emission cross-sections (α_em) were determined. Er/Yb:(Y_0.9La_0.1)₂O₃ ceramics owned broader peaks and longer lifetime (12.3 ms) at 1548 nm due to the glass-like structure of (Y_0.9La_0.1)₂O₃ ceramics. The results showed Y₂O₃ and Y_1.8La_0.2O₃ transparent ceramics are promising gain media for developing the solid-state 1.5 μm optical amplifiers and tunable UC lasers.