Experimental Verification to Obtain Intrinsic Thermal Diffusivity by Laser-Flash Method

There is a need to obtain highly reliable values of thermophysical properties. The thermal conductivity of solids is often calculated from the thermal diffusivity, specific heat, and density, respectively, measured by the laser-flash method, differential scanning calorimetry, and Archimedes’ method. The laser-flash method is one of the most well-known methods for measuring the thermal diffusivity of solids above room temperature. This method is very convenient to measure the thermal diffusivity without contact in a short time. On the other hand, it is considered as an absolute reference measurement method, in particular, because only measurements of basic quantities such as time, temperature, length, and electrical quantities are required, and because the uncertainty of measurement can be analytically evaluated. However, it could be difficult in some cases to obtain reliable thermal-diffusivity values. The measurement results can indeed depend on experimental conditions; in particular, the pulse heating energy. A procedure to obtain the intrinsic thermal-diffusivity value was proposed by National Metrology Institute of Japan (NMIJ). Here, “intrinsic” means unique for the material, independent of measurement conditions. In this method, apparent thermal-diffusivity values are first measured by changing the pulse heating energy at the same test temperature. Then, the intrinsic thermal diffusivity is determined by extrapolating these apparent thermal diffusivities to a zero energy pulse. In order to verify and examine the applicability of the procedure for intrinsic thermal-diffusivity measurements, we have measured the thermal diffusivity of some materials (metals, ceramics) using the laser-flash method with this extrapolation procedure. NMIJ and Laboratoire National de Metrologie et d’essais (LNE) have laser-flash thermal-diffusivity measurement systems that are traceable to SI units. The thermal diffusivity measured by NMIJ and LNE on four materials shows good agreement, although they used different measurement systems and different analysis methods of the temperature-rise curve. Experimental verification on the procedure was carried out using the measured results. Some problems and considered solutions for laser-flash thermal-diffusivity measurements are discussed.