Hot-pressed ZrB2–SiC–YSZ composites with various yttria content: Microstructure and mechanical properties |
| |
Authors: | Weijie Li Xinghong Zhang Changqing Hong Jiecai Han Wenbo Han |
| |
Affiliation: | aCenter for Composite Materials, Harbin Institute of Technology, Harbin 150001, PR China |
| |
Abstract: | ZrB2–10 vol%SiC–20 vol%YSZ composites were prepared by hot-pressed sintering with yttria content ranging from 2 mol% to 8 mol% in YSZ. The phase constitution, microstructure and mechanical properties of the composites were found to be strongly dependent on the yttria content. The average grain size became bigger for the composites with higher yttria content. When the yttria content was below 3 mol%, there is no cubic zirconia in the polished surface of composites, and the flexural strength of the composites was above 740 MPa. With the increase in yttria content, the fracture toughness fell down from 6.4 MPa m1/2 to 5.6 MPa m1/2. Vickers’ hardness of the hot-pressed composites varied above 18 GPa without obvious effect of the yttria content. |
| |
Keywords: | ZrB2– SiC– YSZ composites Yttria content Microstructure Mechanical properties |
本文献已被 ScienceDirect 等数据库收录! |