| Er-Y-Cr-Si化合物在极低温区的巨低场磁热效应（英文） |
| |
| 作者姓名： | 奚磊 郑新奇 高亚伟 许家旺 刘超凡 王鼎淞 徐菊萍 殷雯 杨淑娴 靳宝杰 朱梦媛 许玮峯 申见昕 张静言 黄河 吴燕飞 顾飞 史慧宇 陶怡璇 王守国 沈保根 |
| |
| 作者单位： | 1. School of Materials Science and Engineering,Beijing Advanced Innovation Center for Materials Genome Engineering,University of Science and Technology Beijing;2. School of Materials Science and Engineering,Anhui University;3. Beijing National Laboratory for Condensed Matter Physics,Institute of Physics,Chinese Academy of Sciences & University of Chinese Academy of Sciences;4. Songshan Lake Materials Laboratory;5. Institute of High Energy Physics,Chinese Academy of Sciences;7. Ningbo Institute of Materials Technology and Engineering,Chinese Academy of Sciences |
| |
| 基金项目： | supported by the National Key Research and Development Program of China (2021YFB3501202 and 2019YFB2005800)；;the Science Center of the National Science Foundation of China (52088101)；;the National Natural Science Foundation of China (51871019, 52171170, 52130103, 51961145305, and 51971026)；;the 111 Project (B170003)； |
| |
| 摘 要： | 高性能低温低场磁热材料在气体液化等领域具有重要的应用前景.本团队通过真空电弧熔炼的方式成功合成了一系列多晶Er1-xYxCr2Si2(0≤x≤0.8)样品,这些材料表现出巨大的低场磁热效应.其中Cr含量为0.1的样品显示出最好的低场磁热性能以及接近2 K的合适的工作温区.更重要的是,在0-1 T的磁场变化下,该样品的最大磁熵变峰值以及最大绝热温变峰值分别高达19.2 J kg-1 K-1和4.3 K.其磁熵变峰值为目前已报道的20 K以下温区合金类磁热材料的最大值.通过Arrott曲线,平均场理论以及约化磁熵变曲线等手段,证明了磁相变特征为二级相变.物理机理分析表明,10%的Y替代导致高达15.9%的磁熵变峰值增强的原因在于替代样品所具有的大饱和磁化强度以及小饱和磁场.
|
|
|