| EFFECT OF POTENTIAL ON INTERACTION BETWEEN STRESS CORROSION CRACKING AND CORROSION FATIGUE OF AUSTENITIC STAINLESS STEEL IN BOILING 42% MgCl_2 SOLUTION |
| |
| 引用本文： | FENG Tao CHEN Liangshi KE Wei Corrosion Science Laboratory,Institute of Corrosion and Protection of Metals,Academia Sinica,Shenyang,China. EFFECT OF POTENTIAL ON INTERACTION BETWEEN STRESS CORROSION CRACKING AND CORROSION FATIGUE OF AUSTENITIC STAINLESS STEEL IN BOILING 42% MgCl_2 SOLUTION[J]. 金属学报(英文版), 1991, 4(9): 168-173 |
| |
| 作者姓名： | FENG Tao CHEN Liangshi KE Wei Corrosion Science Laboratory Institute of Corrosion and Protection of Metals Academia Sinica Shenyang China |
| |
| 作者单位： | FENG Tao CHEN Liangshi KE Wei Corrosion Science Laboratory，Institute of Corrosion and Protection of Metals，Academia Sinica，Shenyang，China |
| |
| 摘 要： | The environment-sensitive fracture behaviour of 0Cr18Ni9Ti austenitic stainless steel inboiling 42% MgCl_2 under the specific load of low frequency and high mean stress was inves-tigated from the relations and differences of crack growth rates and fractographs betweenstress corrosion fatigue and stress corrosion cracking.The interaction between stress corro-sion cracking and corrosion fatigue was also studied from fracture characteristics with empha-sis on the effects of applied potential on the interaction.
|
| 收稿时间： | 1991-09-11 |
| 修稿时间： | 1991-09-11 |
EFFECT OF POTENTIAL ON INTERACTION BETWEEN STRESS CORROSION CRACKING AND CORROSION FATIGUE OF AUSTENITIC STAINLESS STEEL IN BOILING 42% MgCl_2 SOLUTION |
| |
| FENG Tao CHEN Liangshi KE Wei Corrosion Science Laboratory. EFFECT OF POTENTIAL ON INTERACTION BETWEEN STRESS CORROSION CRACKING AND CORROSION FATIGUE OF AUSTENITIC STAINLESS STEEL IN BOILING 42% MgCl_2 SOLUTION[J]. Acta Metallurgica Sinica(English Letters), 1991, 4(9): 168-173 |
| |
| Authors: | FENG Tao CHEN Liangshi KE Wei Corrosion Science Laboratory |
| |
| Affiliation: | FENG Tao CHEN Liangshi KE Wei Corrosion Science Laboratory,Institute of Corrosion and Protection of Metals,Academia Sinica,Shenyang,China |
| |
| Abstract: | The environment-sensitive fracture behaviour of 0Cr18Ni9Ti austenitic stainless steel in boiling 42% MgCl_2 under the specific load of low frequency and high mean stress was inves- tigated from the relations and differences of crack growth rates and fractographs between stress corrosion fatigue and stress corrosion cracking.The interaction between stress corro- sion cracking and corrosion fatigue was also studied from fracture characteristics with empha- sis on the effects of applied potential on the interaction. |
| |
| Keywords: | environment-sensitive fracture stress corrosion cracking corrosion fatigue stress corrosion fatigue |