| 低温熔盐法制备片状氧化铝 |
| |
| 引用本文： | 王同乐. 低温熔盐法制备片状氧化铝[J]. 陶瓷, 2011, 0(9): 21-22 |
| |
| 作者姓名： | 王同乐 |
| |
| 作者单位： | 陕西理工学院材料学院,陕西汉中,723003 |
| |
| 摘 要： | 研究了以氢氧化铝为原料，氯化钠一氯化钾为熔盐，以及熔盐加入量对试样物相的影响。研究结果表明，熔盐加入量为67％时，在1000℃保温4h，得到了结晶完整的，边长为5～10μm，厚度为0．6～1．4μm的片状α～Al2O3；熔盐加入量为50％时，不能得到片状氧化铝。
|
| 关 键 词： | 氢氧化铝 氯化钠-氯化钾 制备 片状氧化铝 |
Preparation Plate--Like Alumina in Flux at Low Temperature |
| |
| Wang Tongle. Preparation Plate--Like Alumina in Flux at Low Temperature[J]. Ceramics, 2011, 0(9): 21-22 |
| |
| Authors: | Wang Tongle |
| |
| Affiliation: | Wang Tongle( School of Materials Science and Engineering, Shaanxi, University of Technology, Shaanxi, Hanzhong, 723003 } |
| |
| Abstract: | The effect of flux addition content on product phase was studied, using aluminium hydroxide as raw materials in molten sodium chloride--potassium chloride. The result indicates the crystal plate-like α--Al2O3 were obtained at 1 000℃ for 4h by adding 67% m |
| |
| Keywords: | Aluminium hydroxide Sodium chloride--potassium chloride Preparation Plate--like alumina power |