Electrical conductivity of calcium phosphate ceramics with various Ca/P ratios

Calcium orthophosphate powders with various Ca/P ratios were prepared by a wet process, employing CaCO₃ and H₃PO₄ as starting materials. After they were calcined and pressed to form pellets, they were fired at various temperatures ranging from 800 to 1200 °C. The samples at various stages were examined by X-ray diffraction and SEM, The a.c. electrical conductivity was measured for a series of samples. For some of the samples, the d.c. electrical conductivity and electromotive force were also measured. The samples showed relatively high conductivity (4×10^–5 S cm^–1 at 800 °C). With respect to the tricalcium orthophosphate with nearly stoichiometric composition, the predominant charge carrier at 800 °C was presumed to be an ion although it is not identified at the moment.