| Microstructures of spinodal phases in Cu-15Ni-8Sn alloy |
| |
| 作者姓名： | YanhuiWang MingpuWang BinHong |
| |
| 作者单位： | SchoolofMaterialScienceandEngineering,CentralSouthUniversity,Changsha410083,China |
| |
| 摘 要： | The microstructures of spinodal phases in Cu-15Ni-8Sn alloy were studied by TEM. It was found that when the alloy is completely in a as-quenched state, spinodal decomposition is quick. Ordering appears after spinodal decomposition. The ordered phase with DO22 structure has three variants obtained from coarsening spinodal structure. The reason of ordering appeared after spinodal decomposition is that the content of solute atoms needed by ordering is higher than the average, which can be reached by the composition fluctuation of spinodal decomposition. It was speculated that the morphology of the ordered phase is needle-like.
|
| 关 键 词： | 合金 显微结构 旋节线分解 变量 |
Microstructures of spinodal phases in Cu-15Ni-8Sn alloy |
| |
| YanhuiWang MingpuWang BinHong.Microstructures of spinodal phases in Cu-15Ni-8Sn alloy[J].Journal of University of Science and Technology Beijing,2005,12(3):243-247. |
| |
| Authors: | Yanhui Wang Mingpu Wang Bin Hong |
| |
| Abstract: | The microstructures of spinodal phases in Cu-15Ni-8Sn alloy were studied by TEM. It was found that when the alloy is completely in a as-quenched state, spinodal decomposition is quick. Ordering appears after spinodal decomposition. The ordered phase with DO22 structure has three variants obtained from coarsening spinodal structure. The reason of ordering appeared after spinodal decomposition is that the content of solute atoms needed by ordering is higher than the average, which can be reached by the composition fluctuation of spinodal decomposition. It was speculated that the morphology of the ordered phase is needle-like. |
| |
| Keywords: | Cu-15Ni-8Sn alloy spinodal decomposition DO22 ordering variant |