| 容器钢钢板表面纵裂的产生原因和预防措施 |
| |
| 引用本文： | 梁亚. 容器钢钢板表面纵裂的产生原因和预防措施[J]. 连铸, 2011, 0(1): 45-47 |
| |
| 作者姓名： | 梁亚 |
| |
| 作者单位： | 济南钢铁集团总公司第三炼钢厂,山东济南,250101 |
| |
| 摘 要： | 在生产容器钢的过程中,轧制后的钢板表面有表面纵裂产生,经过数据统计和分析,提出修改钢种成分控制、加热时间等预防措施,取得明显效果。
|
| 关 键 词： | 钢板 表面纵裂 钢种成分 加热时间 |
Causes and Measures of Surface Crack on Vessel Steel Plate |
| |
| LIANG Ya. Causes and Measures of Surface Crack on Vessel Steel Plate[J]. CONTINUOUS CASTING, 2011, 0(1): 45-47 |
| |
| Authors: | LIANG Ya |
| |
| Affiliation: | LIANG Ya(No.3 Steelmaking Plant of Jinan Iron and Steel Co.,Ltd.,Jinan 250101,Shandong,China) |
| |
| Abstract: | Longitudinal cracks appear on the surface of rolled steel plate while producing vessel steel plate.After data statistics and analysis,measures of modifying element control and heating time were proposed and took great effect. |
| |
| Keywords: | plate surface crack element heating time |