Fracture toughness of narrow-gap welded joints in the nuclear pressure vessel steel 22 NiMoCr 37 |
| |
Authors: | I.D. Henderson H.-D. Steffens |
| |
Affiliation: | Institut für angewandte Materialforschung der Fraunhofer-Gesellschaft, D-282, Bremen, Germany |
| |
Abstract: | The mechanical testing of narrow-gap welded joints in 100 and 200 mm thick sections of the steel 22 NiMoCr 37 has revealed that the weld metal, and not the heat affected zone (HAZ) or the weld metal-parent metal boundary. is the critical region. This modified gas-shielded welding process operates with a very low heat input of the order of 6.500 J cm−1 pass−1 and the combination of small diameter welding wires and high welding speeds contributes to the excellent joint properties in the as-welded condition.To investigate the effect of preheating and post-welding heat treatment on the mechanical properties of narrow-gap welds, tensile, notch impact, flat bend and fracture toughness test specimens were extracted from joints welded with the following conditions: (1) no preheating: no post-weld heat treatment; (2) no preheating: soaking at 300°C: (3) no preheating: stress-relief heat treatment at 600°C; (4) preheating 200–250°C; no post-weld heat treatment; (5) preheating 200–250°C; soaking at 300°C; (6) preheating 200–250°C; stress relief heat treatment at 600°C. Tensile testing at room temperature and at 250°C of round specimens oriented across the seam revealed the ultimate fracture to be always located in the base material remote from the welded zone. Although pores or slag inclusions had an influence on bend-test results of specimens in the as-welded condition, the results generally show failure free bends to 180°C with no evidence of cracking in the HAZ or at the fusion boundary.Using sharp-notched impact bend specimens with the notch located in the centre of the seam as well as in and across the HAZ, absorbed energy-test temperature curves have been determined for each welding condition. In comparison with the base material impact toughness, the weld exhibits superior toughness in the temperature range − 60 – 0°C, but yielded lower values at room temperature. After stress relieving at 600°C, the impact toughness of the weld reduced significantly, apparently due to precipitations occurring in the weld-metal microstructure. Test results from welded specimens with the no notch in the HAZ show this region to have superior notch impact toughness to the base material.Crack opening displacement (COD) specimens 45 × 90 × 380 mm with the fatigue crack located in the weld metal and in the HAZ were tested at 0 and 20°C using both the recommendation in BS DD 19: 1972 as well as acoustic emission measurements for the determination of COD values. For this method of fracture toughness testing it has been shown that the occurrence of a critical event must be clearly defined as corresponding to stable crack growth or alternatively to unstable crack propagation. |
| |
Keywords: | |
本文献已被 ScienceDirect 等数据库收录! |
|