Liquid phase behavior and its effect on crystalline morphology in the extruded poly(ethylene terephthalate)/poly(ethylene-2,6-naphthalate) blend

Morphology in an extruded poly(ethylene terephthalate)/poly(ethylene-2,6-naphthalate) was investigated using time-resolved light scattering, optical microscope and small-angle X-ray scattering. During annealing at 280 °C, the domain structure via spinodal decomposition preceded, the transesterification followed, and then the transesterification between the two polyesters induced the dissolution of the liquid-liquid (L-L) phase separation, i.e. the homogenization. The annealed specimen for various time periods (t_s) at 280 °C was subjected to a temperature-drop to 120 °C for the isothermal crystallization and then the effects of liquid phase morphology on crystallization was investigated. With t_s, the H_ν (cross-polarization) light scattering patterns exhibited the dramatic change from a four-leaf clover pattern with maximum intensity at azimuthal angle 45° (×-type scattering pattern) to a diffuse pattern of circular symmetry and then a four-leaf clover pattern with maximum intensity at azimuthal angles 0 and 90° (+-type scattering pattern). This suggests that the crystalline structure depends on the level of the block and/or random copolymer produced by the transesterification during annealing. The H_ν scattering patterns reflected differences in the principle polarizability of the crystalline lamellae with respect to the spherulitic radius. On the other hand, the long period L_B, an average distance between two adjacent crystalline lamellae, increased with t_s at 280 °C. The dependence of L_B on t_s was explained by the change in the crystallization rate G.