Improvement of the critical current density in Bi-2223 ceramics by sodium–silver co-doping

Bi_1.46Pb_0.36Ag_0.18Sr₂Ca₃Cu_4?xNa_xO_y (x = 0, 0.05, 0.1 and 0.25) samples were prepared by a conventional solid state reaction method. The prepared samples are characterized using X-ray powder diffraction, scanning electron microscope, dc electrical resistivity and magnetic-hysteresis loop measurements. It has been shown that the Na doping in low contents significantly improves the physical properties of Bi-2223 phase. Magnetic hysteresis measurements have shown that the largest hysteresis curve belongs to Bi_1.46Pb_0.36Ag_0.18Sr₂Ca₃Cu_3.95Na_0.05O_y sample including x = 0.05 Na content, indicating that it has best flux pinning capability in samples produced in this work. In addition, J_c values of the samples were calculated from the hysteresis loop measurement by using the Bean’s model showing that J_c increases with small amounts of sodium–silver co-doping.