Comparison of retardation behaviour of 2024-T3 and 7075-T6 Al alloys

Retardation in fatigue crack growth rate following the application of single and periodic tensile overloads was studied for 2024‐T3 and 7075‐T6 aluminium alloys. Tests were performed at constant stress and at constant stress intensity factor ranges, at a load ratio of R= 0.1, at a baseline ΔK in the 10–20 MPa√m range which corresponds to the Paris regime. Overload ratios of 1.3–1.65 were studied with overload spacing, n, varying from 20 to 10 000 cycles. 2024‐T3 displayed an order of magnitude higher retardation, N_d, due to single tensile overloads compared to 7075‐T6. Periodic overloads induced maximum retardation when n/N_d≈ 0.5 for both alloys, the magnitude being only 15% higher for 2024‐T3.