| 底吹氮气冶炼高氮不锈钢的应用研究 |
| |
| 引用本文： | 赵定国,王书桓.底吹氮气冶炼高氮不锈钢的应用研究[J].特殊钢,2012,33(5):15-18. |
| |
| 作者姓名： | 赵定国 王书桓 |
| |
| 作者单位： | 河北联合大学冶金与能源学院教育部现代冶金技术重点实验室，唐山063009 |
| |
| 基金项目： | 国家自然科学基金项目资助(50974051) |
| |
| 摘 要： | 根据对高氮不锈钢冶炼设备和工艺、氮气在高温高压下溶入钢液中的方式和特点,以及底吹增氮的优势的分析,在实验室通过300 g钢水底吹异型坩埚在0.5～1.5 MPa,氮气底吹流量0.14～0.24 m~3/h,1820～1910 K下对高氮不锈钢Cr18Mn18N(/%:0.17C、18.00Cr、18.09Mn、0.25Si、0.010S、0.020P、1.07N)进行增氮试验。结果表明,在1.5 MPa、1890 K,0.15 m~3/h底吹氮气流量下,当底吹时间20～30 min氮含量趋于饱和,可快速冶炼出氮含量≥1.0%高氮不锈钢,具有良好的工艺效果。
|
| 关 键 词： | 高氮不锈钢Cr18Mn18N 高压 底吹氮 氮含量 |
| 收稿时间： | 2012-03-27 |
Applied Research on High Nitrogen Stainless Steel Smelting by Bottom-Blowing Nitrogen |
| |
| Zhao Dingguo
,
Wang Shuhuan.Applied Research on High Nitrogen Stainless Steel Smelting by Bottom-Blowing Nitrogen[J].Special Steel,2012,33(5):15-18. |
| |
| Authors: | Zhao Dingguo Wang Shuhuan |
| |
| Affiliation: | Educational Ministry Key Lab of Modem Metallurgy Technology, College of Metallurgy and Energy, Hebei United University, Tangshan 063009 |
| |
| Abstract: | Based on the analysis on the smelting units and processes for high nitrogen stainless steel, the mode and character of nitrogen dissolving into liquid at high temperature-high pressure and the advantage of adding nitrogen by bottom-blowing nitrogen, in laboratory the adding nitrogen test for high nitrogen stainless steel Crl8Mnl8N (/% : 0. 17C, 18. 00Cr, 18. 09Mn, 0. 25Si, 0. 010S, 0. 020P, 1. 07N) is carried out by a 300g liquid bottom-blowing shaped crucible with 0. 5 -1.5 MPa, nitrogen bottom-blowing rate 0. 14 ~0. 24 m3/h at 1 820 ~ 1 910 K. Results show that with 1. 5 MPa and nitrogen bottom-blowing rate 0. 15 m3/h at 1 890 K, as bottom-blowing for 20 ~30 min, the nitrogen content in liquid tends to saturation, it is available to quick-smelt high nitrogen stainless steel in which the nitrogen content is more than 1. 0%. The bottom-blowing technology has nice process effect. |
| |
| Keywords: | |