Sintering behaviour of La1−xSrxFeO3−δ mixed conductors |
| |
Authors: | Lise T Sagdahl Mari-Ann Einarsrud Tor Grande |
| |
Affiliation: | aDepartment of Materials Science and Engineering, Norwegian University of Science and Technology, 7491 Trondheim, Norway |
| |
Abstract: | The sintering properties of La1−xSrxFeO3−δ (x = 0.1, 0.25) mixed conductors have been investigated with particular emphasis on the effect of secondary phases due to cation non-stoichiometry (±5 mol% La excess and deficiency). Secondary phases, located at grain boundaries in cation non-stoichiometric materials, increased the sintering temperature compared to single-phase materials. Extensive swelling in final stage of sintering was observed in all materials, which resulted in micro-porous materials. The swelling was most pronounced in the phase pure and two-phase materials due to La-deficiency, while refractory secondary phases in La-excess materials inhibited both sintering, grain growth and swelling. In La-deficient materials, formation of molten secondary phases resulted in rapid swelling due to viscous flow. The present findings demonstrated the importance of controlling sintering temperature and time, as well as careful control of the cation stoichiometry of La1−xSrxFeO3−δ in order to achieve fully dense and homogenous La1−xSrxFeO3−δ ceramics. |
| |
Keywords: | Perovskites Sintering Porosity Membranes Fuel cells (La Sr)FeO3 |
本文献已被 ScienceDirect 等数据库收录! |
|