Enhanced hydrogen storage properties of 4MgH2 + LiAlH4 composite system by doping with Fe2O3 nanopowder

In this paper, the hydrogen storage properties and reaction mechanism of the 4MgH₂ + LiAlH₄ composite system with the addition of Fe₂O₃ nanopowder were investigated. Temperature-programmed-desorption results show that the addition of 5 wt.% Fe₂O₃ to the 4MgH₂ + LiAlH₄ composite system improves the onset desorption temperature to 95 °C and 270 °C for the first two dehydrogenation stage, which is lower 40 °C and 10 °C than the undoped composite. The dehydrogenation and rehydrogenation kinetics of 5 wt.% Fe₂O₃-doped 4MgH₂ + LiAlH₄ composite were also improved significantly as compared to the undoped composite. Differential scanning calorimetry measurements indicate that the enthalpy change in the 4MgH₂–LiAlH₄ composite system was unaffected by the addition of Fe₂O₃ nanopowder. The Kissinger analysis demonstrated that the apparent activation energy of the 4MgH₂ + LiAlH₄ composite (125.6 kJ/mol) was reduced to 117.1 kJ/mol after doping with 5 wt.% Fe₂O₃. Meanwhile, the X-ray diffraction analysis shows the formation of a new phase of Li₂Fe₃O₄ in the doped composite after the dehydrogenation and rehydrogenation process. It is believed that Li₂Fe₃O₄ acts as an actual catalyst in the 4MgH₂ + LiAlH₄ + 5 wt.% Fe₂O₃ composite which may promote the interaction of MgH₂ and LiAlH₄ and thus accelerate the hydrogen sorption performance of the MgH₂ + LiAlH₄ composite system.