H2 production via water gas shift in a composite Pd membrane reactor prepared by the pore-plating method

In this work, H₂ production via catalytic water gas shift reaction in a composite Pd membrane reactor prepared by the ELP “pore-plating” method has been carried out. A completely dense membrane with a Pd thickness of about 10.2 μm over oxidized porous stainless steel support has been prepared. Firstly, permeation measurements with pure gases (H₂ and N₂) and mixtures (H₂ with N_2, CO or CO₂) at four different temperatures (ranging from 350 to 450 °C) and trans-membrane pressure differences up to 2.5 bar have been carried out. The hydrogen permeance when feeding pure hydrogen is within the range 2.68–3.96·10⁻⁴ mol m⁻² s⁻¹ Pa^−0.5, while it decreases until 0.66–1.35·10⁻⁴ mol m⁻² s⁻¹ Pa^−0.5 for gas mixtures. Furthermore, the membrane has been also tested in a WGS membrane reactor packed with a commercial oxide Fe–Cr catalyst by using a typical methane reformer outlet (dry basis: 70%H₂–18%CO–12%CO₂) and a stoichiometric H₂O/CO ratio. The performance of the reactor was evaluated in terms of CO conversion at different temperatures (ranging from 350 °C to 400 °C) and trans-membrane pressures (from 2.0 to 3.0 bar), at fixed gas hourly space velocity (GHSV) of 5000 h⁻¹. At these conditions, the membrane maintained its integrity and the membrane reactor was able to achieve up to the 59% of CO conversion as compared with 32% of CO conversion reached with conventional packed-bed reactor at the same operating conditions.