| 连铸板坯角部裂纹分析与改善措施 |
| |
| 引用本文： | 张建新,王豫东,吾塔,于辉,刘奉家. 连铸板坯角部裂纹分析与改善措施[J]. 新疆钢铁, 2011, 0(2): 33-36 |
| |
| 作者姓名： | 张建新 王豫东 吾塔 于辉 刘奉家 |
| |
| 作者单位： | 1. 宝钢集团八钢公司制造管理部
2. 新疆八一钢铁股份有限公司 |
| |
| 摘 要： | 文章主要针对包晶钢,亚包晶含铌、钒微合金钢连铸板坯角部频繁出现横裂纹的现象进行分析.通过分类统计,分析其成因,提出了改进措施,连铸板坯的角部横裂纹得到了有效控制.
|
| 关 键 词： | 连铸板坯 二次冷却 工艺控制 |
Analysis and Improving Measurements of Transversal Crack in Continuous Casting Slab Corner |
| |
| ZhANG Jian-xin,WANG Yu-dong,WU Ta,YU Hui,LIU Feng-jia. Analysis and Improving Measurements of Transversal Crack in Continuous Casting Slab Corner[J]. Xinjiang Iron and Steel, 2011, 0(2): 33-36 |
| |
| Authors: | ZhANG Jian-xin WANG Yu-dong WU Ta YU Hui LIU Feng-jia |
| |
| Affiliation: | ZhANG Jian-xin 1,WANG Yu-dong 2,WU Ta1,YU Hui 2,LIUFeng-jia 1(1.ManufacturingManagement Department,Bayi Iron&Steel Co.,Baosteel Group,2.XinjiangBayi Iron&Steel Stock Co.,Ltd. |
| |
| Abstract: | The phenomena that transversal cracks frequently occurred in continuous casing slab(CCS) corners of peri-tectic steel,hypo-peritectic steel and vanadium micro-alloyed steel is analyzed.Improving measurements are put forward through classification statistic,and finally the transversal cracks on CCS corners are controlled effectively. |
| |
| Keywords: | CCS secondary cooling technics control |