Dielectric and piezoelectric properties of KCT added (Li0.02(Na0.56 K0.46)0.98(Nb0.81Ta0.15Sb0.04)O3 ceramics

In this study, Li_0.02(Na_0.56 K_0.46)_0.98](Nb_0.81Ta_0.15Sb_0.04)O₃ + x mol% K_5.4Cu_1.3Ta₁₀O₂₉ ceramics were fabricated by conventional solid-state solution processes. Then, their dielectric and piezoelectric properties were investigated. Sinterability of all samples was enhanced because K_5.4Cu_1.3Ta₁₀O₂₉ (abbreviated as KCT) acted as sintering aids. As the result of XRD, phase structure showed orthorhombic symmetry when KCT ≤ 0.2 mol%. Whereas, the phase structure changed from orthorhombic symmetry to tetragonal symmetry when KCT?≥?0.4 mol%. The results suggest that the orthorhombic and tetragonal phases co-exist in the composition ceramics with 0.2 mol% < KCT < 0.4 mol% at room temperature. The effects of the addition of KCT on the dielectric and piezoelectric properties were investigated. As the result, excellent properties of density=4.81g/cm³], electromechanical coupling factor (k_p)=0.48 and piezoelectric constant(d₃₃)=252pC/N] were obtained in the composition ceramics with 0.4 mol%KCT.