| 高强度管线钢的抗氢致裂纹性能 |
| |
| 引用本文： | 李云涛,杜则裕,孙娈芬,陶勇寅.高强度管线钢的抗氢致裂纹性能[J].钢铁研究学报,2008,20(12):50-0. |
| |
| 作者姓名： | 李云涛 杜则裕 孙娈芬 陶勇寅 |
| |
| 作者单位： | 1. 天津理工大学材料科学与工程学院, 天津 300191；2. 天津大学材料科学与工程学院, 天津 300072； 3. 河北石油管道技术学院, 河北 廊坊 065000；4. 中国石油管道学院, 河北 廊坊 065000； 5. 中国石油天然气管道科学研究院, 河北 廊坊 065000 |
| |
| 摘 要： | 耐蚀性是影响管道可靠性的重要因素，其中氢致裂纹是管道的失效形式之一。笔者依据NACE TM0284 96 HIC试验标准，对不同组份、不同成形工艺的管线钢的抗氢致裂纹性能进行了测试，研究了珠光体组织偏析带及C、Mn、S元素对管线钢氢致裂纹性能的影响。结果表明：随珠光体偏析带组织的产生，管线钢抗氢致裂纹性能下降；碳含量增加，将增强氢致裂纹敏感性；同时，Mn、S易造成低温组织、夹杂物和聚合物的偏析，将导致管线钢氢致裂纹敏感性的增强。
|
| 关 键 词： | 管线钢 氢致裂纹 带状组织 合金元素 |
| 收稿时间： | 1900-01-01; |
Resistance to HIC of High Grade Pipeline Steels |
| |
| LI Yun-tao,DU Ze-yu,SUN Luan-fen,TAO Yong-yin.Resistance to HIC of High Grade Pipeline Steels[J].Journal of Iron and Steel Research,2008,20(12):50-0. |
| |
| Authors: | LI Yun-tao DU Ze-yu SUN Luan-fen TAO Yong-yin |
| |
| Affiliation: | 1. School of Materials Science and Engineering, Tianjin University of Technology, Tianjin 300191, China; 2. School of Materials Science and Engineering, Tianjin University, Tianjin 300072, China;3. College of Petro Hebei Vocation Technology, Langfang 065000, Hebei, China;4. College of Petro Pipeline China, Langfang 065000, Hebei, China;5. Pipeline Research Institute of CNPC, Langfang 065000, Hebei, China |
| |
| Abstract: | Corrosion resistance play an important role in the reliability of pipeline steels, and HIC (Hydrogen Induced Cracking) is one of failure forms for pipeline. The standard NACE TM0284 96 was adopted to study HIC of pipeline steels with different chemical composition and different fabrication method. The effect of pearlite bands and C, Mn, S on HIC was discussed, the more the pearlite bands, the lower the resistance to HIC, and HIC will develop along the banding microstructure. Moreover, with the increase of elements C, Mn,S, the resistance to HIC will be decreased, meanwhile, Mn and S easily form inclusions, segregation bands that will lead to HIC. |
| |
| Keywords: | pipeline steels HIC banding microstructure alloying element |