Preparation of microfiltration membrane supports using coarse alumina grains coated by nano TiO2 as raw materials

To increase the mixing uniformity of coarse alumina grains with a small amount of nano TiO₂ particles, TiO₂ particles were prepared on the surface of coarse Al₂O₃ grains by in-situ hydrolysis of TiCl₄. The coated coarse Al₂O₃ powder was used to prepare microfiltration membranes supports. The effects of TiO₂ content and sintering temperatures on the bending strength, porosity and pore size distribution of the obtained supports were studied. The results show that the melted nano TiO₂ grains locate mainly at the neck of Al₂O₃ grains, which increases the bending strength of the support by increases the neck area. However, the bending strength is weakened if the TiO₂ content is excessive. No aggregated nano TiO₂ grainsare found. The resulting supports sintered at 1650 °C for 2 h yields a bending strength of 55.4 MPa, a porosity of 38% with a mean pore size of 8.0 μm.