Microstructure and strength of the TiAl/40Cr joint diffusion-bonded with Ti-V-Cu filler metal |
| |
引用本文: | 冯吉才,何鹏,钱乙余,韩杰才,张秉刚. Microstructure and strength of the TiAl/40Cr joint diffusion-bonded with Ti-V-Cu filler metal[J]. 中国焊接, 2002, 11(2): 148-150 |
| |
作者姓名: | 冯吉才 何鹏 钱乙余 韩杰才 张秉刚 |
| |
作者单位: | StateKeyLaboratoryofAdvancedWeldingProductionTechnology,HarbinInstituteofTechnology,Harbin150001 |
| |
摘 要: | In this study,intermetallic TiAl and steel 40Cr diffusion bonded successfully by using a composite barrien layer Ti/V/Cu,In this case,a diphase Ti3Al TiAl layer and a Ti solid solution which enhance the strength of the joint are obtained at the TiAl/Ti interface.The interface of TiAl/Ti/V/Cu/40Cr was free from intermetallic compounds and other brittle phases,and the strength of the joint was as high as 420MPa,very close to that of the TiAl base.This method gives a reliable bonding of intermetallic TiAl and steel 40Cr.
|
关 键 词: | 扩散结合 显微结构 钛铝合金 40Cr 钛钒铜焊丝 |
Microstructure and strength of the TiAl/40Cr joint diffusion-bonded with Ti-V-Cu filler metal |
| |
Abstract: | In this study, intermetallic TiAl and steel 40Cr are diffusion bonded successfully by using a composite barrien layer Ti/V/Cu. In this case, a diphase Ti3Al+TiAl layer and a Ti solid solution which enhance the strength of the joint are obtained at the TiAl/Ti interface. The interface of TiAl/Ti/V/Cu/40Cr was free from intermetallic compounds and other close to that of the TiAl base. This method gives a reliable bonding of intermetallic TiAl and steel 40Cr. |
| |