碳含量对C-276合金组织及晶间腐蚀敏感性的影响 |
| |
引用本文: | 李艳美,王明家,张斌,张爽,刘聪,马忠仁,万志永. 碳含量对C-276合金组织及晶间腐蚀敏感性的影响[J]. 有色金属科学与工程, 2020, 11(4): 56-63. DOI: 10.13264/j.cnki.ysjskx.2020.04.009 |
| |
作者姓名: | 李艳美 王明家 张斌 张爽 刘聪 马忠仁 万志永 |
| |
作者单位: | 1.秦皇岛核诚镍业有限公司,河北 秦皇岛 066200 |
| |
摘 要: | 选取不同碳含量的C-276合金板材样品,先对样品进行固溶处理,随后在900 ℃下进行不同时间的敏化处理。采用ASTM G28中A法,对固溶及敏化后的C-276样品进行晶间腐蚀敏感性试验,得出C-276材料的晶间腐蚀年腐蚀率随敏化时间的增加而增加,即延长敏化时间会增加C-276合金的晶间腐蚀敏感性。固溶状态下,高碳型C-276合金晶间腐蚀敏感性高于低碳型C-276合金;而在900 ℃敏化30 min以后,低碳型C-276合金呈现出更高的晶间腐蚀敏感性。采用金相显微镜和扫描电镜(SEM)研究碳含量对C-276合金显微组织的影响,固溶态下,低碳型合金晶界和晶粒内部均未发现有明显析出相,而高碳型C-276合金在部分晶界和晶粒内部分布着颗粒状富含Mo的析出相μ相。敏化过程中,无论低碳还是高碳型C-276合金,其析出相均为富含Mo的M6C型碳化物。高碳型C-276合金中,由于μ相对Mo元素起到钉扎作用,导致富含Mo的碳化物析出速度减缓,因此在敏化后,高碳型C-276合金具有更低的晶间腐蚀敏感性。
|
关 键 词: | C-276合金 敏化处理 晶间腐蚀 碳化物 析出相 |
收稿时间: | 2020-07-09 |
Effect of carbon content on microstructure and intergranular corrosion susceptibility of C-276 alloy |
| |
Affiliation: | 1.Qinhuangdao Hecheng Nickle Co., Ltd., Qinhuangdao 066200, Hebei, China2.Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004, Hebei, China3.CITIC Dicastal Co., Ltd., Qinhuangdao, Qinhuangdao 066011, Hebei, China |
| |
Abstract: | Samples of different carbon content C-276 alloy plate were selected. The samples were solution treated first, and then sensitized at 900 ℃ for different times. The method A of ASTM G28 was used to test the intergranular corrosion of C-276 samples with solution and sensitization. The results showed that the annual corrosion rate of C-276 alloy increased with the increase of sensitization time, and the intergranular corrosion sensitivity of C-276 alloy increased with the increase of sensitization time. The intergranular corrosion sensitivity of high carbon type C-276 alloy is higher than that of low carbon type C-276 alloy in solid solution state. After sensitization at 900 ℃ for 30 minutes, low carbon C-276 alloy shows higher intergranular corrosion sensitivity. The effect of carbon content on the microstructure of C-276 alloy was studied by metallographic microscope and scanning electron microscope (SEM). In the solution state microstructure of low carbon C-276 alloy, no obvious precipitates were found at the grain boundary and inside the grains. In the solution state microstructure of high carbon C-276 alloy, the precipitated phase μ phase rich in Mo is distributed in part of the grain boundary and inside the grain. No matter low carbon or high carbon C-276 alloy, the precipitated phase in sensitization process is Mo rich M6C carbide. In the high carbon C-276 alloy, the precipitation rate of Mo rich carbides is slowed down due to the pinning effect of μ on Mo. Therefore, low carbon C-276 alloy has higher intergranular corrosion sensitivity after sensitization. |
| |