The influence of solvent type and polymer concentration on the physical properties of solid state polymerized PA66 nanofiber yarn |
| |
| Authors: | Razieh Hashemi Sanatgar Sedigheh Borhani Seyed Abdolkarim Hosseini Ravandi Ali Akbar Gharehaghaji |
| |
| Affiliation: | 1. Department of Textile Engineering, Nanotechnology and Advanced Materials Institute, Isfahan University of Technology, 84156 83111 Isfahan, Iran;2. Department of Textile Engineering, Amirkabir University of Technology, Tehran, Iran |
| |
| Abstract: | We investigated the effects of two different solvent types and three solution concentrations on the electrospinning of solid state polymerized polyamide 66 (SSP PA66) nanofiber yarns. Nanofiber yarns were electrospun from SSP PA66 solutions in formic acid and formic acid/chloroform (3/1), using two oppositely metallic spinnerets system. Scanning electron microscopy (SEM) and X‐ray diffraction (XRD) were employed to characterize the morphology and properties of the nanofibrous yarns. Experimental results show that adding chloroform to formic acid as a binary solvent increases viscosity of polymer solution and the nanofibers diameter significantly. XRD patterns reveal that the presence of chloroform affects the crystallinity and the mechanical properties of the produced nanofibrous yarns. PA66 nanofiber yarn from 10 wt % formic acid/chloroform (3/1) solution was successfully electrospun with strength and modulus of 120.16 MPa and 1216.27 MPa respectively. It is also shown that the solution concentration has a significant effect on the modulus of the nanofibers yarns. © 2012 Wiley Periodicals, Inc. J Appl Polym Sci, 2012 |
| |
| Keywords: | nanotechnology nanofibers yarn solid state polymerized polyamides mechanical properties X‐ray diffractometry scanning electron microscopy solvent type solution concentration |
|
|