Fabrication of Porous Ceramics with Unidirectionally Aligned Continuous Pores |
| |
| Authors: | Guo-Jun Zhang Jian-Feng Yang Tatsuki Ohji |
| |
| Affiliation: | Synergy Materials Research Center, National Institute of Advanced Industrial Science and Technology (AIST), Nagoya 463—8687, Japan |
| |
| Abstract: | Porous alumina ceramics with unidirectionally aligned continuous pores were fabricated via the slurry coating of fugitive fiber. Cotton thread was coated with ceramic slurry by pulling it through the slurry, and specimens were produced by spooling the coated thread. The obtained porous alumina ceramics had an average pore diameter of 165 μm, 35% open porosity, and a bending strength of 160 MPa. It was suggested that the pore size and the porosity could be adjusted using the diameter of the cotton thread and the solids concentration of the slurry, respectively. |
| |
| Keywords: | pores/porosity alumina processing |
|
|