Dynamic mechanical properties of semi‐interpenetrating polymer network‐based on nitrile rubber and poly(methyl methacrylate‐co‐butyl acrylate)

In this article, semi‐interpenetrating polymer network (Semi‐IPNs) based on nitrile rubber (NBR) and poly(methyl methacrylate‐co‐butyl acrylate) (P(MMA‐BA)) were synthesized. The structure and damping properties of the prepared Semi‐IPNs blends were characterized and by fourier transform infrared spectrum (FTIR), dynamic mechanical analysis (DMA), scanning electron microscopy (SEM), thermogravimetric analysis (TGA/DTG), and tensile mechanical properties. The results showed that interpenetrating network based on P(MMA‐BA) and NBR was successfully obtained, which showed the improved thermal stability compared to NBR/P(MMA‐BA)‐based two‐roll mill blends. Furthermore, Semi‐IPNs showed significantly better the dynamic mechanical properties than that of the two‐roll mill system. With the increasing feed ratio of BA and MMA during the preparation of Semi‐IPNs, the loss peak position for P(MMA‐BA) in NBR/PMMA IPNs shifted to a lower temperature from 20°C to ?17°C, and when NBR in Semi‐IPNs was accounted for 40 wt %, the dynamic mechanical thermal analysis showed that much more advanced damping material with wider temperature range (?30°C < T < 80°C) as tan δ > 0.45 can be achieved. Therefore, it was expected as a promising way to obtain the excellent damping materials with good oil‐resisted properties according the Semi‐IPNs system. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014 , 131, 40217.