Materials characterization of WNxCy, WNx and WCx films for advanced barriers

A ternary WN_xC_y system was deposited in a thermal ALD (atomic layer deposition) reactor from ASM at 300 °C in a process sequence using tungsten hexafluoride (WF₆), triethyl borane (TEB) and ammonia (NH₃) as precursors. The WC_x layers were deposited by a novel ALD process at a process temperature of 250 °C. The WN_x layers were deposited at 375 °C using bis(tert-butylimido)-bis-(dimethylamido)tungsten (^tBuN)₂(Me₂N)₂W (imido-amido) and NH₃ as precursors. WN_x grows faster on plasma enhanced chemical vapor deposition (PECVD) oxide than WC_x does on chemical oxide. WN_xC_y grows better on PECVD oxide than on thermal oxide, which is opposite of what is seen for WN_x. In the case of the ternary WN_xC_y system, the scalability towards thinner layers and galvanic corrosion behavior are disadvantages for the incorporation of the layer into Cu interconnects. ALD WC_x based barriers have a low resistivity, but galvanic corrosion in a model slurry solution of 15% peroxide (H₂O₂) is a potential problem. Higher resistivity values are determined for the binary WN_x layers. WN_x shows a constant composition and density throughout the layer.