Synthesis and characterization of YAG:Ce<sup>3+</sup> fluorescence powders by co-precipitation method |
| |
Authors: | HU Yucai Lü Yimin YU Xuehua ZHOU Li YU Junsheng |
| |
Affiliation: | 1(1.State Key Laboratory of Electronic Thin Films and Integrated Devices;School of Optoelectronic Information,University of Electronic Science and Technology of China(UESTC),Chengdu 610054,China;2.School of Chemistry and Material Science,Ludong University,Yantai 264025,China;3.School of Chemical Engineering,Shandong University of Technology,Zibo 255049,China) |
| |
Abstract: | YAG:Ce3+(Yttrium aluminum garnet) fluorescence powders were successfully prepared by co-precipitation method using aluminum nitrate,yttrium nitrate,cerous nitrate as the starting materials and ammonium carbonate as precipitant.The products were characterized by X-ray powder diffraction,luminescence spectrometer,transmission electron microscope(TEM).The XRD results showed that the obtained YAG:Ce3+ fluorescence powders had the crystalline structures of YAG at calcinations temperature of 900 oC and the TEM results showed that the grain diameters were about 100 nm.The YAG:Ce3+ fluorescence powders,synthesized by co-precipitation method,had the best luminescence property when the Ce doping amount was x=0.06 in the molecular formula of Y3-xCexAl5O12,the calcinations time was 2 h and the calcinations temperature was 1000 °C. |
| |
Keywords: | YAG:Ce3+ powders co-precipitation method characterization luminescence property rare earths |
本文献已被 维普 等数据库收录! |
|