奥氏体化温度对40CrNiMo钢组织和性能的影响
引用本文:熊国源,刘利华,朱文涛. 奥氏体化温度对40CrNiMo钢组织和性能的影响[J]. 中国冶金, 2021, 31(7): 30-37. DOI: 10.13228/j.boyuan.issn1006-9356.20210174
作者姓名:熊国源  刘利华  朱文涛
作者单位:中信戴卡股份有限公司, 河北 秦皇岛 066011
摘    要:详细研究了奥氏体化温度对中碳调质钢40CrNiMo的淬透性、以0.7℃/s淬火后组织及调质处理后组织和性能的影响.研究结果显示,随着奥氏体化温度从800提高至1000℃,材料的淬透性逐渐增加,尤其是当奥氏体化温度提高至950℃以后,淬透性增加幅度显著变大.当奥氏体化温度为800℃时,组织中存在相对多的铁素体,使得淬火后...

关 键 词:调质钢  奥氏体化  淬透性  组织  性能

Effect of austenizing temperature on microstructure and mechanical properties of 40CrNiMo steel
XIONG Guo-yuan,LIU Li-hua,ZHU Wen-tao. Effect of austenizing temperature on microstructure and mechanical properties of 40CrNiMo steel[J]. China Metallurgy, 2021, 31(7): 30-37. DOI: 10.13228/j.boyuan.issn1006-9356.20210174
Authors:XIONG Guo-yuan  LIU Li-hua  ZHU Wen-tao
Affiliation:CITIC Dicastal Co., Ltd., Qinhuangdao 066011, Hebei, China
Abstract:Effect of austenizing temperature on hardenability, microstructure of 40CrNiMo steel after quenching at a cooling rate of 0.7 ℃/s and microstructure and mechanical properties of 40CrNiMo steel after tempering was studied. Results showed that with increasing temperature from 800 to 1 000 ℃, the hardenability was increased gradually, especially when the temperature exceeded 950 ℃. When the austenitizing temperature was 800 ℃, there was some ferrite in the microstructure, resulting in lower hardness but higher toughness. When the austenitizing temperature was 900 ℃, the specimen possessed the highest strength but the ductility was lower. The fracture mechanism was also changed with increasing temperature, especially for impact specimens. All tensile specimens exhibited ductile fracture with dimples in the fracture surface. However, impact specimens changed from dimple fracture to cleavage or quasi-cleavage fracture, with more typical river pattern in the fracture surface when the austenitizing temperature exceeded 900 ℃.
Keywords:quenched and tempered steel  austenitizing  hardenability  microstructure  mechanical property   