Bulk p-CuInSe2 photo-electrochemical solar cells

Dense CuInSe₂ of high quality, prepared by the fusion technique in evacuated quartz ampoule from stoichiometric melt, crystallizes in the chalcopyrite structure. Compositional analysis carried out by secondary ion mass spectrometry (SIMS) and energy dispersive spectroscopy (EDS) indicates a uniform distribution of elements through the depth and a composition close to the stoichiometry. The diffuse reflectance spectrum gives a band gap at 0.94 eV. The electrical conductivity follows an Arrhenius-type law with activation energy of 23 meV in conformity with polarons hopping. Above 320 °C, CuInSe₂ undergoes an irreversible oxidation. The thermal variation of the thermopower indicates p-type behavior attributed to copper deficiency and a hole mobility μ_300 K of 0.133 cm² V⁻¹ s⁻¹, thermally activated. In KCl media, the compound exhibits an excellent chemical stability with a corrosion rate of 8 μmol cm⁻² month⁻¹. The photo-electrochemical properties, investigated for the first time on the ingots, confirm the p-type conductivity. From the capacitance measurements, the flat band potential (V_fb=−0.62V_SCE) and the holes density (N_A=4×10¹⁷ cm⁻³) were determined. The valence band, located at 4.43 eV below vacuum, is made up of mainly Se orbital with little admixture of Cu character. The change of the electrolyte causes a variation in the potential V_fb (dV_fb/dpH=−0.058 V pH⁻¹) indicating strong OH⁻ adsorption. The fill factor in S²⁻ media was found to be 0.54; such result was corroborated by semi-logarithmic plots.