| 连铸坯表面裂纹产生原因分析 |
| |
| 引用本文： | 王冲. 连铸坯表面裂纹产生原因分析[J]. 中国科技博览, 2014, 0(35): 37-38 |
| |
| 作者姓名： | 王冲 |
| |
| 作者单位： | [1]内蒙古科技大学机械工程学院,内蒙古包头014010; [2]包钢集团国际经济贸易有限公司,内蒙古包头014010 |
| |
| 摘 要： | 铸坯表面质量的好坏直接影响最终轧制产品，针对包钢CSP所生产的Q345B热轧板坯出现的裂纹缺陷，阐述了影响铸坯表面纵裂纹、横裂纹形成的原因及防止表面裂纹产生的技术措施。
|
| 关 键 词： | 连铸坯 裂纹缺陷 技术措施 |
Cause Analysis for Surface Crack of Continuous Casting |
| |
| Wang Chong. Cause Analysis for Surface Crack of Continuous Casting[J]. ZHONGGUO BAOZHUANG KEJI BOLAN, 2014, 0(35): 37-38 |
| |
| Authors: | Wang Chong |
| |
| Affiliation: | Wang Chong (1. Mechanical Engineering School in Inner Mongolia University of Science and Technology, Baotou, Inner Mongolia 014010; 2. International Economic ＆ Trade Company, Ltd. in Baotou (Group) Iron ＆ Steel Company ,Baotou, Inner Mongolia 014010) |
| |
| Abstract: | The quality of Slab surface directly defect on final rolling product, Aiming at the crack defect of Q345B hot rolled plate at Baotou CSP, Reasons effecting on forming vertical crack and transversal crack on surface of continuous casting slab are simply discussed and technological measures to prevent surface crack are expound. |
| |
| Keywords: | Continuous casting slab Crack defect Technological measure |