Critical Microstructures for Microcracking in Al2O3-ZrO2 Composites

The internal strains asSociated with the martensitic phase transformation of zirconia were used to introduce microcracks into Al₂O₃/ZrO₂ composites. The degree of transformation was found to be dependent on the volume fraction of ZrO₂ and its size, the latter of which could be controlled by suitable heat treatments. The microstructural changes that occurred during the heat treatments were studied using quantitative microscopy and X-ray diffraction. For materials containing more than 7.5 vol% Zr0₂, the ZrO₂ particles were found to pin the Al₂O₃ grain boundaries, thus limiting the Al₂O₃ grain growth. The limiting grain size was found to be dependent on size and volume fraction of ZrO₂. Heat treatments for the higher volume fraction materials (>7.5 vol% ZrO₂) caused micro-structural changes which resulted in increased amounts of monoclinic ZrO₂ at room temperature; elastic modulus measurements indicated that this was occurring concurrently with microcracking. By combining the ZrO₂ grain-size distributions with the X-ray analysis it was possible to calculate the critical ZrO₂ size required for the transformation. The critical size was found to decrease with increasing amounts of ZrO₂. Hardness and indentation fracture toughness were measured on the composites. Grain fragmentation was observed at the edge of the indentations and microcracks were observed directly, using an AgNO₃ decoration technique, near the indentations.