| Abstract: | The microstructure of ultrahigh molecular weight polyethylene (UHMW-PE) sheets biaxially drawn in the molten state was investigated by means of wide angle X-ray diffraction (WAXD), small angle X-ray scattering (SAXS), differential scanning calorimetry (DSC), and electron microscopy. The crystallographic c-axis tended to be oriented in the sheet plane by the biaxial drawing in the molten state. The microstructure of the biaxially drawn UHMW-PE was shown to depend upon molecular weight of UHMW-PE. The biaxially drawn sheet of higher molecular weight (Mv = 2,700,000) showed a fibrous structure, while the lower molecular weight sample (Mv 700,000) had a lamellar structure. The result of DSC measurements suggested that a small number of nucleating extended chain crystals was produced by biaxial melt drawing of the UHMW-PE sheet with higher molecular weight. |