| Abstract: | Wood pulp fibers possess strength and modulus properties which compare favorably with glass fibers when the differences in fiber densities are considered. Softwood pulp fibers with fiber aspect ratios near 100 are readily dispersed into high-density polyethylene or isotactic polypropylene with the aid of carboxyic dispersing agents to form mixtures containing 50 weight-percent wood pulp which can be readily injection molded. The mechanical properties of the molded specimens were similar for all types of pulp including Kraft (bleached and unbleached), mechanical and chemical-mechanical pulps, waste pulps, and reclaim newspapers. Comparisons of the stiffness/weight efficiencies revealed that pulp composites equal or exceed the stiffness of most traditional materials of construction including steel, aluminum, glass-fiber composites, and talefilled polyolefins, while retaining a major material cost advantage. The measured strength values of the pulp composites were less than the theoretically predicted values due to the presence of voids created by the formation of volatiles during processing. Mechanical pulps which were available in dry form were preferred because of lower cost and ease of handling. Wood fibers are non-abrasive so that relatively large concentrations may be incorporated into polyolefins without causing serious machine wear during mixing and fabrication. |