Hot-pressing and characterization of TiB2–SiC composites with different amounts of BN additive

This research aimed to study the influence of different amounts of hBN additive on the mechanical properties and microstructure of TiB₂-15 vol% SiC samples. All ceramics, containing 0, 3.5, and 7 vol% hBN, were sintered at 2000 °C using a hot-pressing route and reached their near full densities. Thanks to two different chemical reactions among the SiC reinforcement and the TiB₂ surface oxides (B₂O₃ and TiO₂), the in-situ phases of SiO₂ and TiC were generated over the sintering process. The intergranular mode was identified as the predominant fracture type in all three composite samples. The hBN additive could contribute to grain refining of composites so that the sample containing 7 vol% hBN reached the finest microstructure. Finally, the highest Vickers hardness of 25.4 HV_0.5 kg and flexural strength of 776 MPa were attained for the TiB₂–SiC and TiB₂–SiC-7 vol% hBN samples, respectively.