In-vitro heat-generating and apatite-forming abilities of PMMA bone cement containing TiO2 and Fe3O4

Poly (methyl methacrylate) (PMMA) bone cement is widely used as a filler for repairing bone defects. To improve the effectiveness of the treatment for bone defects caused by metastatic bone tumours, we propose the formulation of PMMA cement containing titania (TiO₂) and magnetite (Fe₃O₄) that offers high bone affinity, making the cement suitable for use in magnetic hyperthermia. The TiO₂ and Fe₃O₄ contents of the PMMA cement varied from 20 to 45 mass%. The various cement samples were evaluated for their apatite-forming ability and heat-generation characteristics. The samples containing TiO₂ in concentrations of 15 mass% or higher formed apatite on their surfaces within 14 days in a simulated body fluid. The heat-generation characteristics of the samples were evaluated by applying an alternating current (AC) magnetic field under the following conditions: |H| = 40 Oe and f = 600 kHz, or |H| = 100 Oe and f = 100 kHz. The surface temperatures of the samples containing 25 and 30 mass% Fe₃O₄ reached 42.3 and 44.8 °C, respectively, at |H| = 40 Oe and f = 600 kHz. During hyperthermia treatment, cancer cells die at temperatures higher than 42 °C, and the cement samples fabricated in this study could reach this temperature. However, since some degree of heat loss will occur in vivo, it is necessary to ensure that the temperature is higher than 42 °C by varying the AC magnetic field. Nevertheless, the fact that the samples containing Fe₃O₄ concentrations of 25 mass% or higher generated enough heat under the AC magnetic field makes them suitable for clinical use in hyperthermia. Thus, PMMA cement containing 15 mass% or more of TiO₂ and 25 mass% or more of Fe₃O₄ should be investigated as a bioactive bone cement with a strong hyperthermia effect.