Microstructure and mechanical behaviour of transient liquid phase spark plasma sintered B4C–SiC–TiB2 composites from a B4C–TiSi2 system

Almost fully-dense B₄C–SiC–TiB₂ composites with a high combination of strength and toughness were prepared through in situ reactive spark plasma sintering using B₄C and TiSi₂ as raw materials. The densification, microstructure, mechanical properties, reaction, and toughening mechanisms were explored. TiSi₂ was confirmed as a reactive sintering additive to promote densification via transient liquid-phase sintering. Specifically, Si formed via the reaction between B₄C and TiSi₂ that served as a transient component contributed to densification when it melted and then reacted with C to yield more SiC. Toughening mechanisms, including crack deflection, branching and bridging, could be observed due to the residual stresses induced by the thermoelastic mismatches. Particularly, the introduced SiC–TiB₂ agglomerates composed of interlocked SiC and TiB₂ played a critical role in improving toughness. Accordingly, the B₄C–SiC–TiB₂ composite created with B₄C-16 wt% TiSi₂ achieved excellent mechanical performance, containing a Vickers hardness of 33.5 GPa, a flexural strength of 608.7 MPa and a fracture toughness of 6.43 MPa m^1/2.