M- S-H formation in MgO-SiO2slurries via wet milling for magnesia based castables

It is believed that the formation of hydration phase, MgO-SiO₂-H₂O (M-S-H), contributes to good workability and reliable comprehensive properties for magnesia based castables. In order to stimulate the formation of M-S-H in magnesia based castables and understand the minimum introduction of microslica amount, wet milling process was used to promote the dissolution of MgO and SiO₂ in this work. The slurry containing different content of microsilica with wet milling technology and the castables with/without wet milling slurry were prepared. The effects of microsilica content on the formation of hydration phases were analyzed by XRD, FT-IR and TG/DSC and the properties of magnesia based castables were evaluated by explosion resistance, CMOR, HMOR and so on. The results showed that the formation of M-S-H was accelerated because of the dissolution of Mg²⁺ and HSiO₃^? in wet milling process. Higher amount of M-S-H led to a tight bonding in the early stage, and a denser structure after firing at high temperature due to the limited formation of brucite and in-situ formation of evenly distributed forsterite phase. In addition, much higher HMOR were obtained when less microsilica was added, attributing to the suppressed formation of low-melting-point liquid. Therefore, 2–3 wt% microsilica addition was recommended in this process.