Dielectric temperature stability of Nb-modified Bi0.5(Na0.78K0.22)0.5TiO3 lead-free ceramics

In this study, the phase structure, microstructure and dielectric properties of Bi_0.5(Na_0.78K_0.22)_0.5(Ti_1-xNb_x)O₃ lead-free ceramics prepared by traditional solid phase sintering method were studied. The second phase pyrochlore bismuth titanate (Bi₂Ti₂O₇) was produced in the system after introduction of Nb⁵⁺. The dielectric constant of the sample (x = 0.03) sintered at 1130 °C at room temperature reached a maximum of 1841, and the dielectric loss was 0.045 minimum. It had been found that the K⁺ and Nb⁵⁺ co-doped Bi_0.5Na_0.5TiO₃ (BNT) lead-free ceramics exhibited outstanding dielectric-temperature stability within 100–400 °C with T_cc ≤±15%. Result of this research provides a valuable reference for application of BNT based capacitors in high temperature field.